(1)鉗口夾持質量對5052鋁板拉伸品質起著決定性的作用，鉗口的均勻夾持使板材縱向每一個單元都被拉伸到等量長度，從而實現均勻拉伸，起到了對板材的矯直作用。
(1) The clamping quality of the jaw plays a decisive role in the tensile quality of 5052 aluminum plate. The uniform clamping of the jaw makes each unit of the plate be stretched to the same length in the longitudinal direction, so as to realize the uniform stretching and straighten the plate.
(2)拉伸機機架的剛度與預變形補償的影響：由于板材拉伸機的兩個拉力缸  等量安置在兩側，對于橫截面越大的板材，在拉伸過程中機架產生的變形也越大。因此，拉伸機機架應保持更大的剛度，設計與制造中應考慮機架預變形償，以克服和補償拉伸過程中機架產生的變形。
(2) Influence of frame stiffness and pre deformation compensation: because the two tension cylinders of the plate drawing machine are equally placed on both sides, the larger the cross section of the plate, the greater the deformation of the frame during the drawing process. Therefore, the frame of the drawing machine should maintain greater stiffness, and the pre deformation compensation of the frame should be considered in the design and manufacture, so as to overcome and compensate the deformation of the frame during the drawing process.

(3)拉伸前5052鋁板板材尺寸的不規則性和應力分布的不均勻性，拉伸過程中有效地控制平穩的速度，使各個變形單元得以充分均勻地變形，是滿足均勻拉伸的重要
(3) Before drawing, the size of 5052 aluminum plate is irregular and the stress distribution is non-uniform. In the drawing process, it is important to control the smooth speed effectively so that each deformation unit can deform fully and evenly
(4)實踐證明，長度相對小一些，寬度相對大一些的板材，其橫向展平效果  條件之一要好得多。生產中應選擇寬、長比大一些的工藝方案。
(4) Practice has proved that the transverse flattening effect of plates with relatively small length and large width is much better. In the production, the process plan with larger ratio of width to length should be selected.
(5)對淬火后變形較大的板材，應利用輥式矯直機初步矯平，而后在拉伸機上進行終的精矯平。
(5) For the plate with large deformation after quenching, the roller straightener should be used for preliminary leveling, and then the final fine leveling should be carried out on the drawing machine.
(6)由于拉伸機的主要作用是消除板材的殘余應力，以縱向小變形量的塑性  變形過程為主，因而對縱向有更好的矯直作用，對橫向平直度的改善能力非常有限。
(6) Because the main function of the drawing machine is to eliminate the residual stress of the plate, the plastic deformation process with small longitudinal deformation is the main process, so it has a better straightening effect on the longitudinal direction, and its ability to improve the transverse flatness is very limited.